Synthesis and structural-adsorption characteristics of MMS/MFI materials obtained from titanoaerosil
Анотація
A method has been proposed of the one-stage bitemplate synthesis of mesoporous zeolite containing materials on the basis of Ti-aerosil (Ti-MZ), also the kinetics is studied of their formation and texture features. The materials obtained have been characterized by methods of IR-spectroscopy (FTIR), X-ray diffraction (XRD) and adsorption of nitrogen.
Посилання
Сушко P.В., Воронин Е.Ф., Чуйко А.А. Исследование высокодисперсных смешанных оксидов SiO2-TiO2 // Журн. физ. химии. – 1979. – Т. 53, № 9. – С.2395–2396.
Изучение структурных превращений в титаносодержащих кремнезёмах / Р.В. Сушко, А.В. Гетте, И.Ф. Миронюк, А.А. Чуйко // Журн. прикл. химии. – 1983. – Т. 56, № 6 – С.1230–1234.
О структуре поверхности синтетического титанокремнезема / В.И. Зарко, Ю.И. Горлов, В.В. Брей, А.А. Чуйко // Теорет. и експерим. химия. – 1986. – Т. 22, № 2. – С.220–242.
Huang L., Guo W., Deng P., Xue Z., Li Q. Investigation of Synthesizing MCM-41/ZSM-5 Composites // Phys. Chem. B. – 2000. - V. 104, N 2. – P.2817-2823.
Karlsson A., Stocker M., Schmidt R. Composites of micro- and mesoporous materials: simultaneous syntheses of MFI/MCM-41 lice phases by a mixed template approach // Micropor. Mesopor. Mater. – 1999. – V. 27, N 2. – P.181-186.
On D.T., Kaliaguine S. Large Pore Meesoporous Materials with Semi-Crystalline Zeolitic Frameworks // Angew. Chem. Int. Ed. – 2001. – V. 40, N 3. – P.3248-3251.
On D. T., Lutic D., Kaliaquine S. An example of mesostructured zeolitic material: UL-TS‑1 // Micropor. Mesopor. Mater. – 2001. – V. 44, N 6. – P.435-441.
Liu Y., Pinnavaia T.J. Assembly of Hydrothermally Stable Aluminosilicate Foams and Large-Pore Hexagonal Mesostructures from Zeolite Seeds under Strongly Acidic Conditi-ons // Chem. Mater. – 2002. – V. 14, N 1. – P.3-10.
Liu J., Zhang X., Han Y., Xiao F.S. Direct Observation of Nanorange Ordered Microporo-sity within Mesoporous Molecular Sieves // Chem. Mater. – 2002. – V. 14, N 3. – P.2536-2542.
Liu J., Zhang X., Pinnavaia T.J. Steam-Stable MSU-S Aluminosilicate Mesostructures Assembled from Zeolite ZSM-5 and Zeolite Beta Seeds // Angew. Chem. Int. Ed. – 2001. - V. 40, N 2. – P.1255-1258.
Cartlidge S., Nissen H.U., Wessicken R. Ternary mesoporous structure of ultrastable zeolite // Zeolites – 1989. – V. 5, N 6. – P.346-349.
Goto Y., Fukushima Y., Ratu R. et al. Mesoporous Material from Zeolite // J. Porous Mater. – 2002. – V. 9, N 1 - P.43-48.
Corma A., Diaz U., Domine M.E., Vornes V. AlITQ-6 and TiITQ-6: Synthesis, Characteri-sation, and Catalytic Activity // Angew. Chem. Int. Ed. – 2000. – V. 39, N 2. - P.1499-1501.
Corma A., Fornes V., Rey F. Delaminated Zeolites: An Efficient Support for Enzymes // Adv. Mater. – 2002. – V. 14, N 1. – P.71-74.
Kalliaguine S., On D.T. Mesoporous zeolitic material with microporous crystalline mesopore walls / US Patent № 6 669 924, 2003.
Плюснина И.И. Инфракрасные спектры силикатов. - М.: Изд-во МГУ, 1967. - 188 с.
Fenelonov V.B., Romannikov V.N., Derevyankin Z.Yu. Mesopore size and surface area calculations for hexagonal mesophases (types MCM-41, FSM-16, etc.) using low-angle XRD and adsorption data // Micropor. Mesopor. Mater. - 1999. - V. 28, N 1. - P.57-72.
- Автори залишають за собою право на авторство своєї роботи та передають журналу право першої публікації цієї роботи на умовах ліцензії Creative Commons Attribution License, котра дозволяє іншим особам вільно розповсюджувати опубліковану роботу з обов'язковим посиланням на авторів оригінальної роботи та першу публікацію роботи у цьому журналі.
- Автори мають право укладати самостійні додаткові угоди щодо неексклюзивного розповсюдження роботи у тому вигляді, в якому вона була опублікована цим журналом (наприклад, розміщувати роботу в електронному сховищі установи або публікувати у складі монографії), за умови збереження посилання на першу публікацію роботи у цьому журналі.
- Політика журналу дозволяє і заохочує розміщення авторами в мережі Інтернет (наприклад, у сховищах установ або на особистих веб-сайтах) рукопису роботи, як до подання цього рукопису до редакції, так і під час його редакційного опрацювання, оскільки це сприяє виникненню продуктивної наукової дискусії та позитивно позначається на оперативності та динаміці цитування опублікованої роботи.